Investigation the Effect of Increasing Board Density and Amount of UF Resin on Particleboard Properties

Document Type : Research Paper

Authors

Abstract

In order to investigation the effect of increasing board density and amount of UF resin on particleboard properties, this study was carried out. .Regarding two variable parameters: board density at three level (520, 620 and 720Kg/m3) and percentage of UF resin (6, 7, and 8%),one layer particleboards with16mm nominal thickness were manufactured. Physical and mechanical properties such as MOR, MOE, IB and thickness swelling (after 24 hours immersion in water) were measured. The results showed that with increase in board density from 520 to 720 Kg/m3, MOR and MOE were increased and dimensional stability were improved. But increase in board density had no significant effect on IB. The results of contour plots showed that manufacturing boards with density of 600-650 Kg/m3and 6% UF resin, all of mechanical properties were maintained in standard specified limits related to those boards and using adequate amount of water resistant materials will Cause improving of thickness swelling after 24 h immersion

Keywords

References

1- امیری، س؛ ١٣٧٧. بررسی اقتصادی کارخانه های تخته خرده چوب، مجله منابع طبیعی ایران، جلد ٥١ ، شماره١، صفحه ٢٥-٣٥.
2- جزایری، ر؛ خادمی اسلام، ح؛ حاجی حسنی، ر؛ نوربخش، ا؛ کارگر فرد، ا؛1387 . بررسی اثر  میزان مصرف چسب، درجه حرارت و زمان پرس بر خواص تخته خرده چوب ساخته شده از چوب گونه Acacia salicina نشریه تحقیقاتعلوم چوب و کاغذ ایران، جلد 23 ، شماره 2 ، صفحه 177-169 .
3- حبیبی، م؛ حسینخانی، ح؛ مهدوی، س؛1386. بررسی اثر زمان پرس و مقدار چسب بر ویژگی های تخته فیبر نیمه سنگین (MDF) ساخته شده از کلش برنج، نشریه تحقیقات علوم چوب و کاغذ ایران، جلد 22، شماره1 ، صفحه61-51.
4- دوست حسینی، ک ؛ ١٣٨٦ . فناوری تولید و کاربرد صفحات فشرده چوبی، انتشارات دانشگاهتهران؛ ٦٤٨ صفحه.
5- روشنی زرمهری، ع؛ 1368 . بررسی استفاده از گونه های تاغ و صنوبر در ساخت تخته خرده چوب. پایان نامه کارشناسی ارشد، دانشکده منابع طبیعی، دانشگاه تهران.
6- عنایتی، ع؛ 1388. جزوه  درسی تخته فیبر پیشرفته. دانشکده منابع طبیعی، دانشگاه تهران.
7- نور بخش، ا؛ کارگر فرد، ا؛ 1385. اثر دانسیته و زمان پرس بر ویژگی های تخته خرده چوب عایقی از گونه صنوبر. مجله تحقیقات علوم چوب و کاغذ ایران، جلد 21، شماره2، صفحه122-115 .
8- Ashori, A., Nourbakhsh, A. 2008. Effect of press cycle and particleboard made from the unde utilized low-quality raw materials. Industrial crops and products.28.225-230.
9- Canadido, L. S., Satio, F., 1990. Influence of strand thickness and board density on the orthotropic properties of oriented strand board. Journal of the japan wood.; Tokyo, V. 36,N.8, p. 632-636.
10- European Standard EN 310. 1993, Wood Based Panel. Department of modulus of elasticity in bending and of bending strength. CEN European Committee for Standardization. Brussels. Belgium.
11- European Standard EN 312-2,1996. Particleboard Specifications part2: requirements for general purpose boards for use in dry conditions. CEN European Committee for Standardization. Brussels. Belgium.
12- European Standard EN 312-3,1996. Particleboard Specifications part3: requirements for boards for interior fitments (including furniture) for use in dry conditions. CEN European Committee for Standardization. Brussels. Belgium.
13- European Standard EN 312-4,1996. Particleboards Specifications part4: requirements for load-bearing boards for use in dry conditions. CEN European Committee for Standardization. Brussels. Belgium.
14- European Standard EN 317. 1993, Particleboard and fiberboards. Determination of swelling in thickness after immersion in water. European Committee for Standardization. Brussels. Belgium.
15- European Standard EN 319. 1993, Determination of tensile strength perpendicular to the plane of the board. CEN European Committee for Standardization. Brussels. Belgium.
16- European Standard EN 326-1. 1993, Wood based panels. Sampling, cutting and inspection. Sampling and cutting of test pieces and expression of test results.
17- Hiziroglu, S., Jarusombuti, S., Fuengrivat, V., Bauchongkol, P., Soontonbura, W.,Darapak, T., 2005. Properties of bamboo- rice straw- eucalyptus composite panels. Forest Prod. J. 55(12), 221- 225.
18- Lehmann, L., Heebink., 1977. Factor affecting Particleboard pressing time Interaction with catalyst system. VSDA for, serv. Res. Pap. FPL. 208. For lab. Madison WLS.
19- Moslemi, A. A., 1974. Particleboard, Vols. 1 and 2. SourthenillionisUniu. Press Carbondale, lllinois.
20- Nemli, G., 2002. Factors affecting the production of E 1 type particleboard. Turk. J. Agric. For. 26 (1), 31-36.
21- Nemli, G., Zekovic, E., Aydin, I., 2007. Some of the parameters influencing surface roughness of particleboard. Building and environment Journal.40 (10) 1337-1340.
22- Neusser ¸H., Krames¸V., Haidinger¸ K., and Serentschy¸ W.,1969.The character of particle and its influence on quality of  surface layers of particleboard.Holzforsch Und Holzverwest.21(4):81-94
23- Zhou, D., 1986. A study of Oriented Strand Board made from hybrid poplar. Holz als Roh-und werk stoff. 48(1990).  29
Iranian Journal of Wood and Paper Industries
Volume 2, Issue 1 - Serial Number 1
January 2012
Pages 103-112

Files

Share

How to cite

Statistics