Tracking and Simulation of Dry Shell Formation in a Wood Drying Process by X-ray Spectroscopy

Document Type : Research Paper

Authors

Abstract

In this research, dry shell formation and receding of evaporation front through the thickness of  beech and spruce boards were investigated during drying using X-ray spectroscopy.
Four surfaces of the boards were coated using epoxy resin to limit moisture flux through the board thickness. The boards were dried using a convectional drying method under the temperature of 60°C and relative humidity of 70%. The scanning process was conducted once in an hour during drying until the dry shell reached the core layer of the boards.
The results revealed that the dry shell was formed faster in the beech board in comparison with the spruce one; however, it reached the core layer of the spruce board in a shorter time. In addition, the pattern of dry shell formation was found to be different between the boards;
a steady-state condition as a result of faster bulk flow of free water was observed during the early stage of drying of the spruce board.
In general, it can be concluded that the controlling factor in the dry shell development to the core layer is water vapor diffusion coefficient of the boards rather than their permeability.

Keywords

References

1- Keey, R.B., Langrish, T.A.G. and Walker, J.C.F., 2000. Kiln-drying of lumber, Springer series, 312p.
2- Remond, R., Mougel, E. and Perre, P., 2005. Using the concept of thin dry layer to explain the evolution of thickness, temperature and moisture content during convective drying of Norway spruce boards, LERMAB (Laboratory of Wood Science), ENGREF, Nancy, France
3- Rosenkilde, A. and Glover, P., 2002. High resolution measurement of the surface layer moisture content during drying of wood using a novel magnetic resonance imaging technique, Holzforschung, 56: 312-317.
4- Rosenkilde, A., Jean Philippe, G. and Amanda, B., 2004. Measurement of moisture content profile during drying of scots pine using magnetic resonance imaging, Holzforshung, 58: 138-142.
5- Wiberg, P. and Moren, T.J.,1999. Moisture flux determination in wood during drying above fiber saturation point using CT-scanning and digital image processing. Holz als Roh-und Werkstoff, 57: 137-144.
6- Wiberg, P., Sehlstedt-Persson, S.M.B. and Moren, T.J., 2000. Heat and mass transfer during sapwood drying above the fiber saturation point, Drying Technology, 18(8): 1647-1664
Iranian Journal of Wood and Paper Industries
Volume 1, Issue 2 - Serial Number 2
December 2011
Pages 1-11

Files

Share

How to cite

Statistics